Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX820 - Americas - (PPE+PA*)-GF20 - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL GTX™ Resin GTX820 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
NORYL GTX™ 820 resin is a 20% glass reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 4000 MPa), excellent chemical resistance, and high heat resistance. NORYL GTX GTX830 resin is an excellent candidate for a wide variety of applications including valves for water management.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 7.1 cm³/10min ISO 1133
温度 280 °C -
荷重 5 kg -
成形収縮率, 平行 0.3 % ISO 294-4, 2577
成形収縮率, 直角 0.9 % ISO 294-4, 2577
ASTM数据
メルトフローレイト, MFI 7 g/10min ASTM D 1238
温度 280 °C -
荷重 5 kg -
成形収縮率., 平行 0.27 mm/mm ASTM D 955
成形収縮率, 直角 0.93 mm/mm ASTM D 955
機械的特性値単位テスト基準
ISO データ
引張弾性率 6400 MPa ISO 527
破壊応力 139 MPa ISO 527
破壊ひずみ 3.6 % ISO 527
曲げ弾性率 5960 MPa ISO 178
シャルピー衝撃強さ, +23°C 62 kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C 8.7 kJ/m² ISO 179/1eA
Izod impact strength, +23°C, 4mm 86 kJ/m² ISO 180/1U
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm 8.8 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 6350 MPa ASTM D 638
破壊応力 133 MPa ASTM D 638
破断伸び 3.6 % ASTM D 638
曲げ弾性率 6030 MPa ASTM D 790
ロックウェル硬度 R 119 - ASTM D 785
ノッチ付きIzod衝撃強さ, 1/8 in 93 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 53 J/m ASTM D 256
温度 -30 °C -
アイゾット衝撃試験, 1/8 in 900 J/m ASTM D 256
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 211 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 248 °C ISO 75-1/-2
ビカット軟化温度, A 252 °C ISO 306
ビカット軟化温度, B 229 °C ISO 306
線膨張係数, 平行 27 E-6/K ISO 11359-1/-2
線膨張係数, 直角 78 E-6/K ISO 11359-1/-2
ASTM数据
ビカット軟化温度 231 °C ASTM D 1525
その他の特性.値単位テスト基準
吸水率. 1.88 % Sim. to ISO 62
密度. 1250 kg/m³ ISO 1183
密度 1240 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 95 - 105 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.07 % -
樹脂温度 280 - 305 °C -
金型温度 75 - 120 °C -
Zone 1 265 - 305 °C -
Zone 2 270 - 305 °C -
Zone 3 275 - 305 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 1.4 MPa -
特殊な特性
成形加工法.
射出成形.
アプリケーション
自動車
領域別の利用可能性
北アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.